项目 | LG-1.0 | LG-0.9 | LG-0.8 | LG-0.7 | LG-0.6 | LG-0.5 |
Al2O3 ％ ≥ | 48 | |||||
Fe2O3 ％ ≤ | 2.0 | |||||
体积密度 g/cm3 ≤ | 1.0 | 0.9 | 0.8 | 0.7 | 0.6 | 0.5 |
耐压强度 Mpa ≥ | 4.0 | 3.0 | 2.5 | 1.8 | 1.0 | 0.8 |
导热系数（W. /m.k）≤. | 0.45 | 0.45 | 0.35 | 0.35 | 0.3 | 0.25 |
永久线变化≤2% ℃ | 1400 | 1400 | 1400 | 1350 | 1350 | 1250 |
项目 | LG-1.0 | LG-0.9 | LG-0.8 | LG-0.7 | LG-0.6 | LG-0.5 |
Al2O3 ％ ≥ | 48 | |||||
Fe2O3 ％ ≤ | 2.0 | |||||
体积密度 g/cm3 ≤ | 1.0 | 0.9 | 0.8 | 0.7 | 0.6 | 0.5 |
耐压强度 Mpa ≥ | 4.0 | 3.0 | 2.5 | 1.8 | 1.0 | 0.8 |
导热系数（W. /m.k）≤. | 0.45 | 0.45 | 0.35 | 0.35 | 0.3 | 0.25 |
永久线变化≤2% ℃ | 1400 | 1400 | 1400 | 1350 | 1350 | 1250 |